Summary：
Nano titanium dioxide XZ-TI01, the appearance of white loose powder. Crystal is anatase, large specific surface area, in light catalysis, solar cells, pressure sensitive resistance, environmental purification, catalyst carrier, lithium battery and gas sensors, etc..
Performance characteristics:
Small particle size, large area, high color, high purity, obvious electrochemical performance. It can be used in lithium titanate battery material and lithium cobalt oxide battery material.
Name
|
Anatase type nano titanium dioxide
|
Model
|
XZ-TI01
|
Appearance
|
White end
|
Particle size
|
10nm
|
PH value
|
6-8
|
specific surface area
|
60-70 m2/g
|
Purity
|
99.9%
|
Dry weight loss
|
105℃、2h ≤ 0.05（%） |
loss on ignition
|
Less than 0.1 (%) |
Iron PPM
|
ore than 3 qualified |
Lead (Pb)
|
Ppm is not more than 10 qualified |
The following is an example of application of nano titanium dioxide:
Industry one: application of pressure sensitive resistance.
The main material of varistor is Zinc Oxide, Zinc Oxide in the two kind of nano titanium adding ratio is 2%, 100 kilograms of varistor materials with nano titanium oxide Zinc Oxide 2 kg, adding nano titanium oxide two varistor materials is a new technology of varistor production, has been widely used in many large varistor production company.
Industry two: battery and gas sensors have been widely used.
Nano titanium dioxide XZ-TI01 as a battery material, its cycling performance is better, has a good fast charge and discharge performance and higher capacity. Adding nano titanium oxide lithium battery, has higher electrochemical reversibility, show pseudocapacitive performance more, without adding is not obvious. Nano titanium dioxide has good quasi metal conductivity and charging and discharging process, including multiple pairs, fast, continuous, reversible Faraday reaction. Its amorphous structure, there are a lot of mixed hydroxyl, and other raw materials have excellent compatibility. Use of lithium titanate material and cobalt acid lithium battery materials, in -0.05 ~ 0.35V (vs SCE) potential range showed typical Faraday pseudocapacitive behavior, the formation of numerous electric double layer capacitance is small; at the same current density (MA / cm2), increase the capacity (A / g); lower self discharge rate, has good cycle life.
Also：
In the air purification using nanometer titanium dioxide photocatalyst XZ-TI01, the production of raw materials, textile industry, bactericidal, anti ultraviolet aging plastic coating, is widely used.
Packing：20 kg / drum lined with plastic film bags.
|